Composition | WC – 50% NiCrBSi – 50% |
Coating Hardness | Nickel 60 HRC Carbides 2000 Hv300 |
ASTM G65 Volume Loss | 3.52 mm3 |
Coating Density | 12 g/cm3 (0.43 lb/in3) |
Coating Porosity | <1% as fused |
Pore Diameter | <1 µm as fused |
Coating Roughness | 10 – 12 µm Ra as sprayed 0.25 – 0.4 µm as fused |
Melting Temperature | 1060°C (1940°F) |