Composition | WC – 28% NiCrBSi – 72% |
Coating Hardness | Matrix 60HRC Carbides 1300Hv300 |
Coating Density | 10.1 g/cm3 (0.36 lb/in3) |
Coating Porosity | <1% as fused |
Pore Diameter | <1µm as fused |
Coating Roughness | –212.5 µm Ra as sprayed 2 – 4 µm as fused |
Melting Temperature | 1060°C (1940°F) |